Fiber-reinforced thermoplastic molding compositions using a copolyester

ABSTRACT

Thermoplastic molding compositions and articles comprise immiscible thermoplastic polymer components and reinforcing fibers. The immiscible thermoplastic polymer components and the fibers are blended together under high shear conditions The molding composition generally contains at least two phases and has an extremely smooth and fiber-free surface. Generally, other very good physical properties are obtained such as high heat distortion temperatures, high tensile modulus, high flex modulus, and the like are also very good. A desired blend of thermoplastic components is thermoplastic polyurethane and polyethylene terephthalate with glass fibers A polyethylene terephthalate copolyester blended with an immiscible thermoplastic polymer, preferably polyurethane, and glass fibers produces thermoplastic molding compositions and articles having surprisingly superior impact strength.

This is a continuation-in-part of Ser. No. 07/759,965 filed Sept. 16, 1991 now U.S. Pat. No. 5,225,476 which is a continuation of Ser. No. 07/490,190 filed Mar. 8, 1990 now abandoned.

FIELD OF THE INVENTION

The present invention relates to thermoplastic molding compositions and more particularly to a blend of y immiscible thermoplastic matrix polymers including a copolyester, which can be readily combined with reinforcing fibers under moderate to high shear to provide a molding composition useful for molding parts substantially free from shrinkage and having very smooth substantially fiber free surfaces and markedly improved impact strength.

BACKGROUND

Thermoplastic polymers combined with glass reinforcing fibers have been used in the past to produce molding compositions capable of being molded under heat and pressure to form plastic molded parts. Blends of thermoplastic polymers were often utilized in an effort to overcome deficiencies in physical properties of one or both thermoplastic polymers. The blends related to compatible or miscible polymers wherein the polymers were mutually soluble or one polymer was soluble in the other. If the two desired polymers were not miscible, then a third solubilizing polymer was added to provide solubilizing characteristics to the two desired polymers and impart compatibility to the overall polymeric mixture.

In the past, in order to obtain a smooth surface on molded plastic parts, a two-component injection molding process has been utilized wherein a second polymeric composition was injected and molded over a first fiber-reinforced polymer to achieve a smooth surface lamina. The two-component molding process, however, is difficult to control and operate in that the two separate molding compositions require controlled extruded ratios of the respective polymers, and the like.

U.S. Pat. No. 4,179,479 to Russell P. Carter, Jr. relates to novel thermoplastic polyurethane materials containing a processing aid More particularly, the patent relates to a thermoplastic polyurethane composition comprising: (A) from 40 to 100 percent by weight of a thermoplastic polyurethane, (B) from 0 to 60 percent by weight of a thermoplastic polymer selected from the group consisting of thermoplastic polycarbonates, thermoplastic polyoxymethylenes, thermoplastic acrylonitrile/butadiene/styrene graft copolymers, thermoplastic polybutylene terephthalates, thermoplastic polyethylene terephthalates, and mixtures thereof and (C) from 0.5 to 10 percent by weight based on the amount of (A) and (B), of a processing aid which is an acrylic polymer having a number average molecular weight of from 500,000 to 1,500,000.

U.S. Pat. No. 4,277,577 to Burg, et al., provides a molding composition of a mixture of an oxymethylene polymer, an elastomer having a softening temperature of below the crystallite melting point of the oxymethylene polymer and a second order transition temperature of from -120° to +30° C., and a segmented thermoplastic copolyester. U.S. Pat. No. 4,369,285 to Sanderson, et al., relates to reinforced thermoplastic molding compositions comprising polyamides and from 0.1 to 10 percent by weight polyurethanes.

U.S. Pat. No. 4,141,879 to Glenn G. McCarroll relates to a thermoplastic material for use under conditions demanding high strength at elevated temperatures, e.g., for under-the-hood automotive or truck components. The material is essentially a three-component alloy of a homopolymer polyamide, a copolymer polyamide, and polyurethane reinforced with a relatively small amount of glass fibers and containing normal amounts of heat stabilizers, ultraviolet screen materials, etc.

U.S. Pat. No. 4,350,799 to Hans G. Schmelzer, et al., relates to a molding composition comprising an intimate, well dispersed blend of thermoplastic polyurethane, thermoplastic polyphosphonate and thermoplastic polycarbonate which composition is characterized by an improved level of flame resistance.

Japanese Publication 61149330, dated Jul. 8, 1986, relates to an injection-molded product having a smooth surface which is prepared from a blend containing 10 parts by weight of polypropylene and 90 parts by weight of inorganic filled polypropylene. There is little, if any, significant change in physical properties.

Additionally it has been surprisingly discovered that when a modified polyethylene terephthalate (PET), as described hereinbelow, is used instead of unmodified PET, it is possible to use a lower processing temperature so as to essentially eliminate degradation of the other thermoplastic polymer during compounding or molding. Even more surprising is the unexpectedly superior improvement in the impact strength of the polymers such that the notched and unnotched Izod impact values are two times or greater for formulations incorporating modified PET (M-PET) over formulations with unmodified PET.

SUMMARY OF THE INVENTION

Molding compositions of the present invention generally relate to two relatively immiscible thermoplastic polymer components. One such component generally has a relatively high viscosity, and the other component a relatively low viscosity at a suitable or desirable processing temperature. At the processing temperature, desirably only minimal degradation, if any, of either component occurs. During processing under usually moderate to high shear conditions, effective amounts of fibers are added to yield generally a two-phase composition having good adhesion between the components as well as good physical properties such as high heat distortion temperatures, high impact resistance, high tensile modulus, high flexural modulus, and the like, as well as very little shrinkage during molding. Although the composition contains fibers therein, the surface of the molded article is generally fiber-free and is extremely smooth. When using modified PET as the relatively high viscosity component, both compounders and end users, such as injection molders, obtain the benefit of widening the processing temperature window. Unexpectedly, the impact strength of the inventive polymers incorporating modified PET is substantially improved over polymers containing unmodified PET.

DETAILED DESCRIPTION OF THE INVENTION

According to the present invention, it has been found that thermoplastic molding compositions having good flow at the processing temperature and typically excellent end-product physical properties can be produced by selecting relatively immiscible thermoplastic polymers and blending or compounding the same under at least moderate shear conditions with reinforcing fibers, and substantially molding the same under high shear conditions such as in injection molding. Although more than two thermoplastic components can be utilized, with the third or additional component being either immiscible or miscible with either of the first two components but compatible with each of said two components, generally only two such components are required. The remaining portion of the specification shall thus often be limited to a discussion of a two-component immiscible system although it is to be understood that additional components can be utilized. By the term "immiscible," it is meant that there are at least two polymer phases as detected by thermal analysis, thermal mechanical analysis, microscopy, or the like.

The shear required in initially blending the thermoplastic polymer components together during or at the compounding stage generally is at least moderate. That is, only enough shear is required to disperse the fibers and the various immiscible polymers to produce generally a two-phase blend. The compounding shear is carried out at a temperature which is similar or the same as the subsequent processing temperature. By the term "two-phase blend," it is meant that one of the thermoplastic polymer components is generally dispersed within the other component such that two separate phases exist, or when a third or additional thermoplastic polymer component is utilized possibly three or more separate phases exist. The amount of shear utilized in the compounding stage is generally at least 5 reciprocal seconds to about 1,000 reciprocal seconds, desirably at least 50 reciprocal seconds to about 700 or 800 reciprocal seconds, and preferably from about 50 reciprocal seconds to about 500 reciprocal seconds, or at any suitable shear rate provided that the fibers are not unduly broken or reduced in size. The compounded molded composition is generally preformed into any conventional shape such as strands, cubes, particles, pellets and the like so that it can subsequently be utilized in a high shear molding apparatus or operation to yield an end product or article. In the forming of the end product or article, a high shear apparatus is utilized such that the shear rate is generally at least 100 reciprocal seconds, desirably at least 500 reciprocal seconds, more desirably at least 800 reciprocal seconds, preferably at least 1,000 reciprocal seconds, up to a value of about 3,000 reciprocal seconds.

Another general requirement of the present invention is that the immiscible thermoplastic polymer component desirably has a relatively dissimilar viscosity at a specific or suitable processing temperature. That is, whenever the two, or more, relatively immiscible thermoplastic polymer components are blended with each other and fibers, one component has a relatively low viscosity in comparison with the other, or more, thermoplastic polymer components which have a generally higher viscosity at the processing or blending temperature. Often the low viscosity thermoplastic polymer component forms a continuous phase, and the high viscosity thermoplastic polymer component forms a discontinuous phase. The difference between viscosities of the high viscosity component, or at least one of the higher viscosity components when two or more such components exist, to the low viscosity component, is generally a ratio of at least 1.5 or 2.0, desirably at least 3.0, and more desirably at least 5.0, and preferably at least 8.0 or 10.0, or even at least 50, at a given processing temperature under generally high shear processing conditions. Although an upper limit is not always necessary, the upper ratio can be 1,000, or less, particularly when the system uses M-PET, for which the upper limit is about 200. Thus, suitable viscosity ranges include any of the above values. Such effective viscosity differences at the processing temperature, along with high shear, contribute to the incorporation of the fibers within the thermoplastic molding compositions and result in a molded article having exceptionally smooth surfaces substantially or essentially and usually completely free of fibers, i.e., at least 95 percent, desirably at least 99 percent, and preferably at least 99.5 percent fiber-free by weight, and usually completely fiber-free.

The end product or article typically has a surface layer which is generally rich in, enriched of, if not entirely composed of, the low viscosity component. The surface layer of the thermoplastic molded article, as noted above, is generally substantially free of fibers with the incorporated fibers thus being located within the interior portion, i.e., below the surface layer, of the molded article. The thickness of the fiber-free surface layer will depend upon the molding conditions, but generally can vary from about 0.5 mils up to about 8-10 mils, or even greater, and usually from about 1.0, 2.0 or 3.0 mils to about 5.0 or 7.0 mils. The mechanism by which the fibers are incorporated within the immiscible components is not fully understood. Nor is it fully understood if a majority of the fibers is incorporated in the relatively high viscosity component(s), the low viscosity component, or both, but it is generally thought that the fibers are located in all of the thermoplastic components. In any event, the interior portion of the thermoplastic molded article is generally a two-phase portion containing the two immiscible thermoplastic polymer components and the fibers, although it may contain three or more phases if three or more thermoplastic polymeric components are utilized with the fibers.

It has been unexpectedly found that when articles or end products of the immiscible thermoplastic polymer components desirably having different viscosities at the processing temperature when blended under high shear conditions have fibers incorporated within the interior portion of the article, blend, etc. such that the surface layer is exceptionally smooth. While not fully understood, the utilization of moderate and preferably high shear, desirably coupled with relative viscosity differences of the immiscible thermoplastic polymer components at the processing temperature to form a thermoplastic molded article, product, etc., unexpectedly yields an article or product having a very smooth surface. The surface smoothness can be measured by a Surtronic Roughness Meter, Model 10, manufactured by Taylor-Hobson. The compositions or blends of the present invention have surface smoothness values of generally 1.0 or 0.9 microns or less, 0.7 microns or less, desirably 0.5 microns or less, preferably 0.4 microns or less, and most preferably 0.3 or 0.02 microns or less are readily obtained. Another advantage of the molding compositions of the present invention is that certain molds which have irregular shapes, cavities, nooks, and the like, are readily filled, often because the low viscosity component tends to promote flow.

A requirement of the immiscible thermoplastic components is that they have minimal, and desirably, no degradation at the suitable or mean processing temperature. Stated differently, the suitable or typical processing temperature is generally below the degradation temperature of all of the polymeric components forming the molding composition. In a TPU/PET system, however, the processing temperature is actually above the degradation temperature of the TPU. It has additionally been discovered that a modified PET having a lower melting temperature, that is, lower than unmodified PET, permits the processing system temperature to be lowered so as to essentially completely avoid degradation of the TPU or other similar relatively higher viscosity polymer with a degradation temperature similar to TPU.

Another important requirement is that the various immiscible thermoplastic components, when blended and especially when molded, are mechanically compatible with each other in that they have good adhesion with respect to one another and to the fibers incorporated therein. Good adhesion is obtained when good physical properties, such as high stiffness and high heat deflection, are achieved.

In general, the molding compositions of the present invention have very good overall physical properties such as high impact resistance, high tensile modulus, high flexural modulus, excellent smoothness, very little, if any, shrinkage upon molding, and the like. Unexpectedly, it has been discovered that a superior improvement in the impact strength of polymers is obtained when the higher viscosity polymer is modified PET.

The polymers utilized in the present invention which typically meet the above requisites are generally true polymers, that is a large molecule built up by the repetition of small, simple chemical units. In other words, the various polymers utilized can be conventional thermoplastic polymers having conventional molecular weights known to the art as well to the literature. A preferred class of one of the immiscible thermoplastic polymer components are the various thermoplastic polyurethanes described hereinbelow with the second immiscible polymer component being polyethylene terephthalate (PET), polyethylene terephthalate glycol (PETG), polycarbonate, polyacetal, and acrylonitrile-butadiene-styrene type copolymers encompassed by the term "ABS". From an overall standpoint, numerous blends of generally two, or more, thermoplastic polymer components can be utilized such as thermoplastic polyurethane, polyethylene terephthalate (PET), polyethylene terephthalateglycol (PETG), polyacetal, polycarbonate, polyvinyl chloride (PVC), copolymers of acrylonitrile-butadiene-styrene (ABS), copolymers of esters and ethers, copolymers of styrene and acrylonitrile (SAN), various polyacrylates, poly(phenylene ether), e.g. (PPO), polysulfones, polybutylene, polyethylene, polypropylene, polystyrene, and the like. Generally, any of at least two of the above-noted types of polymers can be utilized to provide fiber-reinforced thermoplastic molding compositions of the present invention as long as the two, or more, different thermoplastic polymers generally have a dissimilar viscosity at the processing temperature, are molded under high shear conditions, yield at least a two-phase composition, are not subject to degradation, and have good adhesion with respect to one another. A more detailed description of the above thermoplastic polymers is now set forth.

Thermoplastic polyurethanes form a desired and often a preferred class of polymers. Suitable polyurethanes are prepared by reacting a polyisocyanate and one or more chain extenders with an intermediate such as a hydroxyl terminated polyester, a hydroxyl terminated polyether, a hydroxyl terminated polycaprolactone, a hydroxyl terminated polycarbonate (i.e., a polycarbonate polyol), or mixtures thereof, or amine terminated polyesters, polyethers, or polycarbonates, or mixtures thereof.

A preferred class of hydroxyl terminated polyester intermediates is generally a linear polyester having a molecular weight of from about 500 to about 10,000, desirably from about 700 to about 5,000, and preferably from about 700 to about 4,200, and an acid number generally less than 0.8 and preferably less than 0.5. The molecular weight is determined by assay of the hydroxyl groups. The polyester intermediates are produced by (I) an esterification reaction of one or more glycols with one or more dicarboxylic acids or anhydrides, or (2) by transesterification reaction, i.e., the reaction of one or more glycols with esters of dicarboxylic acids. Mole ratios generally in excess of more than one mole of glycol to acid are preferred so as to obtain linear chains having a preponderance of terminal hydroxyl groups.

The dicarboxylic acids can be aliphatic, cycloaliphatic, aromatic, or combinations thereof. Suitable dicarboxylic acids which may be used alone or in mixtures usually have a total of from 4 to 15 carbon atoms and include: succinic, glutaric, adipic, pimelic, suberic, azelaic, sebacic, dodecanoic, isophthalic, terephthalic cyclohexane dicarboxylic, and the like. Anhydrides of the above dicarboxylic acids, such as phthalic anhydride, tetrahydrophthalic anhydride, or the like, can also be utilized, with adipic acid being preferred.

The ester-forming glycols can be aliphatic, aromatic, or combinations thereof; have a total of from 2 to 12 carbon atoms; and include: ethylene glycol, propylene-1,2-glycol, 1,3-propanediol, butylene-1,3-glycol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 2,2-dimethylpropane-1,3-diol, 1,4-cyclohexanedimethanol, decamethylene glycol, dodecamethylene glycol, and the like, with 1,4-butanediol being a preferred glycol.

In addition to the above polyester intermediates, numerous other types of polyester intermediates known to the art and to the literatures can be utilized including those having different molecular weights and/or contain branch polyesters therein. For example poly caprolactone diols can be used. These are known polyester reaction products of lactones and bifunctional compounds having two reactive sites capable of opening the lactone ring. These bifunctional materials may be represented by the formula HX--R--XH wherein R is an organic radical which can be aliphatic, cycloaliphatic, aromatic or heterocyclic and X is O, NH and NR where R is a hydrocarbon radical which can be alkyl, aryl, aralkyl and cycloalkyl. Such materials include diols, diamines and aminoaloohols preferably. Useful diols include alkylene glycols wherein the alkylene group contains 2 to 10 carbon atoms for example, ethylene glycol, 1,2-propane diol, butanediol-1,4, hexamethylene diol-1,6 and the like. Ethylene glycol provides excellent polyesters.

The lactones preferred for preparing the polyesters are epsilon-caprolactones having the general formula ##STR1## wherein at least 6 of the R's are hydrogen and the remainder are hydrogen or alkyl groups containing 1 to 10 carbon atoms, preferably methyl. Mixtures of lactones may be employed to form the polyesters as epsilon-caprolactone and trimethyl-epsilon-caprolactone, "τ" methyl-epsiloncaprolactone, "β"-methyl-epsilon-caprolactone, dimethylepsilon-caprolactone and the like. The lactones are polymerized readily by heating with the bifunctional reactant to a temperature of about 100° to about 200° C. Such polycaprolactone polyols are described in U.S. Pat. No. 3,660,357 which is hereby fully incorporated by reference.

It is noted that suitable polycarbonate polyols can also be utilized as an intermediate, and the same, as well as methods of preparation thereof, are disclosed in U.S. Pat. No. 4,643,949, which is hereby fully incorporated by reference. Other low molecular weight polycarbonate polyol intermediates can also be made from diols such as those set forth hereinabove, including 1,6-hexanediol, and the like, and phosgene; or by transesterification with low molecular weight carbonates such as diethyl or diphenyl carbonate.

The hydroxyl terminated polyethers can be polyether polyols derived from a diol or polyol having a total of from 2 to 15 carbon atoms, preferably an alkyl diol or glycol which is reacted with an ether comprising an alkylene oxide having from 2 to 6 carbon atoms, typically ethylene oxide or propylene oxide, or mixtures thereof. For example, hydroxyl functional polyether can be produced by first reacting propylene glycol with propylene oxide followed by subsequent reaction with ethylene oxide. Primary hydroxyl groups resulting from ethylene oxide are more reactive than secondary hydroxyl groups and thus are preferred. Useful commercial polyether polyols include poly(ethylene glycol), poly(propylene glycol), poly(propylene-ethylene glycol), poly (tetramethylene ether glycol) (PTMEG), copolyethers produced from tetrahydrofuran (THF) and ethylene oxide or THF and propylene oxide, glycerol adduct comprising glycerol reacted with propylene oxide, trimethylolpropane adduct comprising trimethylolpropane reacted with propylene oxide, pentaerythritol adduct comprising pentaerythritol reacted with propylene oxide, and similar hydroxyl functional polyethers. Polyether polyols further include polyamide adducts of an alkylene oxide and can include, for example, ethylenediamine adduct comprising the reaction product of ethylenediamine and propylene oxide, diethylenetriamine adduct comprising the reaction product of diethylenetriamine with propylene oxide, and similar polyamide type polyether polyols. The various polyether intermediates generally have an average molecular weight, as determined by assay of the terminal functional groups, of from about 500 to about 10,000, desirably from about 500 to about 6,000, more desirably from about 500 to about 4,000, and preferably from about 700 to about 3,000.

In addition to the above polyether type intermediates, other intermediates can be utilized known to those skilled in the art as well as to the literature such as those having different molecular weights, made from different reactants, and the like.

The above-mentioned polyols can be used alone or in any combination.

The intermediate, such as a hydroxyl terminated polyester, a polyether, etc., is further reacted with one or more polyisocyanates and preferably a diisocyanate along with an extender glycol, desirably in a "one-shot" process, that is, a simultaneous coreaction of the intermediate, diisocyanate, and extender glycol, to produce a moderate molecular weight linear polyurethane having a melt index of from about 0 to about 150 and preferably from about 0 to about 75 at 230° C, at 2,160 grams. The equivalent amount of diisocyanates to the total amount of hydroxyl and/or amine-containing components, that is, the hydroxyl or amine terminated polyester, polyether, etc., and chain extender glycol, is from about 0.95 to about 1.12 or even 1.20, and desirably from about 0.98 to about 1.06. Alternatively, the urethane can be made in a conventional two-step process wherein initially a prepolymer is made from the polyisocyanate and the intermediate, with the prepolymer subsequently being reacted with the chain extender glycol. The equivalent ratio of the one or more diisocyanates to the hydroxyl or amine terminated intermediate is generally a sufficient amount such that upon subsequent chain extension with a suitable glycol, the overall equivalent ratio of the hydroxyl or amine terminated compounds to the one or more polyisocyanates is approximately 0.95 to about 1.06, and the like. Often it can be an excess such as up to about 1.20 or less, or 1.15 or less. Suitable diisocyanates include non-hindered aromatic diisocyanates such as: 4,4'-methylenebis-(phenyl isocyanate) (MDI); isophorone diisocyanate (IPDI), m-xylylene diisocyanate (XDI), as well as non-hindered cyclic aliphatic diisocyanates such as 1,4-cyclohexyl diisocyanate (CHDI), decane-1,10-diisocyanate, phenylene-1,4-diisocyanate, naphthylene-1,5-diisocyanate, diphenylmethane-3,3'-dimethoxy-4,4'-diisocyanate, dicyclohexylmethane-4,4'-diisocyanate, and cyclohexyl-1,4-diisocyanate, as well as combinations thereof. The most preferred non-hindered diisocyanate is 4,4'-methylenebis(phenyl isocyanate) i.e., MDI.

Suitable extender glycols (i.e., chain extenders) are saturated low molecular weight glycols, preferably aliphatic, and in particular, alkylene glycols containing from 2 to about 12 carbon atoms. These normally have molecular weights not over about 300. Representative glycols include ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, 1,4- butanediol, 1,6-hexanediol, 1,3-butanediol, 1,5-pentanediol, 1,4-cyclohexane-dimethanol, hydroquinone di(hydroxyethyl)ether, diethylene glycol, neopentyl glycol and 3-methyl-1,5-pentanediol, as well as cycloaliphatic and aromatic glycols, and combinations thereof, with 1,4-butanediol being preferred.

In the one-shot polymerization process, a simultaneous reaction occurs between three components: one or more polyol prepolymers, polyisocyanate, and extender glycol. The reaction is generally initiated at temperatures above 100° C. and desirably above 120° C. Inasmuch as the reaction is exothermic, the reaction temperature generally increases to about 200° C. to 280° C. Similar reaction temperatures are utilized when the polyurethane is made in a two-step process.

Examples of the above, as well as other suitable thermoplastic polyurethanes which can be utilized, are set forth in Vol. 13 of the Encyclopedia of Polymer Science and Engineering, John Wiley & Sons, Inc., New York, N.Y., 1988, pages 243-303, which is hereby fully incorporated by reference.

Another specific thermoplastic component which can be utilized is polyethylene terephthalate (PET), known to the art and to the literature, and generally made from the reaction product of ethylene glycol and dimethyl terephthalate or by direct esterification between ethylene glycol and terephthalic acid under heat and a high vacuum. Moreover, PETG polymers can also be utilized, as known to the art and to the literature, and generally are the reaction products of ethylene glycol, a short-chain glycol other than ethylene glycol, and dimethyl terephthalate or terephthalic acid. Examples of other polyesters which can be utilized are set forth in Encyclopedia of Polymer Science and Engineering, Vol. 12, John Wiley & Sons, Inc., New York, N.Y., 1988, pages 217-256, which is hereby fully incorporated by reference.

Another useful class of thermoplastic polymers are polyacetals, i.e., polyoxymethylene, including homopolymers or copolymers thereof which are known to the art and to the literature. Inasmuch as the homopolymer, which is usually made from formaldehyde, must generally be processed at temperatures below about 185° F., copolymers are generally utilized because they have better processing characteristics. Acetal copolymers are made by a reaction between trioxane, a trimer of formaldehyde, and another monomer such as formaldehyde. An example of a commercially available polyacetal copolymer is Celcon, made by Celanese Chemical Company. These and examples of other polyacetals which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 11, John Wiley & Sons, Inc., New York, N.Y., 1988, page 286, which is hereby fully incorporated by reference, as well as in U.S. Pat. Nos. 3,850,873 and 4,017,558, which are also fully incorporated by reference.

Another thermoplastic component is the various polycarbonates, including those which are known to the art and to the literature. Polycarbonates are generally esters derived from a diol, or preferably a dihydric or polyhydric phenol such as bisphenol A, and carbonic acid, phosgene, and the like. Polycarbonates generally have a repeating carbonate group, i.e., ##STR2## and generally always have a ##STR3## radical attached to the carbonate group. Polycarbonates are well known and described in many patents and other technical references. Desirably, the polycarbonate can be characterized by the formula ##STR4## wherein Z is a single bond, an alkylene or alkylidene radical with 1 to 7 carbon atoms, a cycloalkylene or cycloalkylidene radical with 5 to 12 carbon atoms, --O--, --CO--, --SO or SO₂ --, preferably methylene or isopropylidene; R¹ and R² are hydrogen, halogen or an alkylene or alkylidene radical having 1 to 7 carbon atoms; and n equals 0 to 4. Most preferably, the aromatic polycarbonates useful in the practice of the invention have a melt flow rate range of about 1 to 60 gms/10 min. at 300° C., as measured by ASTM D-1238. The most important aromatic polycarbonate which is commercially available from many different sources is the polycarbonate of bis(4-hydroxyphenyl)-2,2-propane, known as bisphenol-A polycarbonate. These and examples of other polycarbonates which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 11, John Wiley & Sons, Inc., New York, N.Y., 1988, pages 648- 718, which is hereby fully incorporated by reference.

Other thermoplastic polymers suitable for use in the present invention are the various ABS type copolymers which are known in the art and to the literature. Such polymers are generally graft copolymers of acrylonitrile, conjugated dienes having from 4 to 8 carbon atoms with butadiene being highly preferred, and a vinyl substituted aromatic having from 8 to about 12 carbon atoms, with styrene being preferred, often referred to as an acrylonitrile-butadiene-styrene copolymer. The amount of the acrylonitrile is generally from about 10 to about 40 percent by weight; the amount of styrene is generally from about 20 to about 70 percent by weight; and the amount of butadiene is generally from about 20 to about 60 percent by weight based upon the total weight of the three-component mixture. Although ABS copolymers are generally a mixture of a styrene-acrylonitrile copolymer and a styrene-acrylonitrile grafted polybutadiene rubber, a terpolymer made from acrylonitrile, butadiene, and styrene monomers can also be used. In lieu of butadiene, other conjugated dienes such as isoprene, pentadiene, dimethylbutadiene, dimethyl pentadiene, and the like can also be utilized. Similarly, in lieu of styrene, vinyl toluene, alpha methyl vinyl toluene, alpha methyl styrene, and the like can be utilized. Although acrylonitrile is normally always utilized, other vinyl cyanides can be utilized such as methacrylonitrile, ethacrylonitrile, and the like. These and examples of other ABS type polymers which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 1, John Wiley & Sons, Inc., New York, N.Y., 1985, pages 388-426, which is hereby fully incorporated by reference.

Another thermoplastic polymer component which can be utilized in the present invention is polyvinyl chloride and the various copolymers thereof which are known to the art and to the literature. Polyvinyl chloride copolymers are generally made from a majority of vinyl chloride monomers and a vinyl component monomer. By the term "vinyl component," it is meant a vinyl-type monomer other than vinyl chloride. Such monomers are well known to the art and to the literature and include esters of acrylic acid wherein the ester portion has from 1 to 12 carbon atoms, for example, methyl acrylate, ethyl acrylate, butyl acrylate, octyl acrylate, cyanoethyl acrylate, and the like; vinyl acetate; esters of methacrylic acid wherein the ester portion has from 1 to 12 carbon atoms, such as methyl methacrylate, ethyl methacrylate, butyl methacrylate, and the like; styrene and styrene derivatives having a total of from 8 to 15 carbon atoms such as alpha methyl styrene, vinyl toluene, chlorostyrene; vinyl; naphthalene; diolefins having a total of from 4 to 8 carbon atoms such as butadiene, isoprene, and including halogenated diolefins such as chloroprene; monoolefins having from 2 to 10 carbon atoms and preferably 2 to 4 carbon atoms; and the like, and mixtures thereof. An amount of vinyl chloride monomer is utilized to produce a copolymer containing at least about 70 percent by weight, and preferably from about 80 to about 93 percent by weight of vinyl chloride repeating units therein. The remainder of the copolymer is made up of the one or more above-noted vinyl component monomers, for example, vinyl acetate. Thus, an amount of vinyl component monomer, when utilized to produce a copolymer, is from up to about 30 percent and preferably from about 7 to about 20 percent by weight of vinyl component repeating units therein. Also included within the definition of the polyvinyl chloride type polymers and copolymers as set forth above are chlorinated polyvinyl chloride polymers (CPVC) and copolymers having a total chlorine content of from about 57 to about 72 percent by weight. These and examples of other polyvinyl chloride type polymers and copolymers which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 17, John Wiley & Sons, Inc., New York, N.Y., 1989, pages 295-376, which is hereby fully incorporated by reference.

Another thermoplastic polymer component which can be utilized in the present invention is a polyester-ether polymer which in reality is a copolyetherester block copolymer generally comprising one or more ring containing polyester blocks as well as one or more acyclic polyether blocks. The polyester block is generally made from an aromatic containing dicarboxylic acid or diester such as terephthalic acid, dimethyl terephthalate, and the like, with a diol generally containing from about 2 to about 10 carbon atoms. The acyclic polyether is generally made from polyalkylene oxide glycols having a total of from about 3 to about 12 atoms including up to about 3 or 4 oxygen atoms with remaining atoms being hydrocarbon atoms. The polyester-ether polymers can be represented by the following formula: (ring containing polyester-b-acyclic polyether). Such polyester-ether copolymers are commercially available such as Hytrel, manufactured by DuPont, and the like, with polybutyleneterephthalate-b-poly(oxytetramethylene) block copolymer being preferred. These and other examples of other polyester-ether copolymers which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 12, John Wiley & Sons, Inc., NY, N.Y., 1988, pages 49-52, which is hereby fully incorporated by reference as well as U.S. Pat. Nos. 2,623,031; 3,651,014; 3,763,109; and 3,896,078.

Another thermoplastic polymer component which can be utilized in the present invention is copolymers of generally styrene and acrylonitrile, typically known as SAN, that is, styrene-acrylonitrile copolymers. Such copolymers can generally be produced by either emulsion, suspension, or continuous mass polymerization, and usually are made from a majority, by weight, of styrene monomers. Comonomers other than styrene which can be utilized include vinyl acetate, methyl acrylate, and vinyl chloride. These and a further detailed description of SAN-type polymers in general are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 1, John Wiley & Sons, Inc., New York, N.Y., 1985, pages 452-470, which is hereby fully incorporated by reference.

Another thermoplastic polymer component which can be utilized in the present invention are the various esters of acrylic or methacrylic acid where the ester portion is typically an alkyl containing from 1 to about 16 carbon atoms, a secondary branched-chain alkyl ester containing from 3 to about 10 carbon atoms, an ester of an olefinic alcohol containing from 3 to about 8 carbon atoms, an aminoalkyl ester containing from about 3 to about 10 carbon atoms, an ester of ether alcohols containing from about 2 to about 10 carbon atoms, a cycloalkyl ester containing from about 4 to about 12 carbon atoms, or a glycol diacrylate containing from about 2 to about 10 carbon atoms, and the like. Very often, copolymers of various acrylates and blends thereof can be utilized. Examples of common, commercially available, acrylates include methyl acrylate, ethyl acrylate, n-butyl acrylate, isobutyl acrylate, 2-ethylhexyl acrylate, and the like. Examples of the various methacrylates include methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, isodecyl methacrylate, stearyl methacrylate, and the like. These and examples of other acrylate or methacrylate esters which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 1, John Wiley & Sons, Inc., New York, N.Y., 1985, pages 234-325, which is hereby fully incorporated by reference.

Another thermoplastic which can be utilized in the present invention is poly(phenylene ether). The most important polymer which can be utilized is poly(2,6-dimethyl-1,4-phenylene ether). Other polymers include poly(2,6-diphenyl-1,4-phenylene ether), poly(2-methyl-6-phenylphenol), as well as copolymers of 2,6-dimethylphenol and 2,6-diphenylphenol. Blends of polystyrene with poly(phenylene ether) can also be utilized. These and examples of other poly(phenylene ether) compounds which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 13, John Wiley & Sons, Inc., NY, N.Y., 1988, pages 1 through 30, which is hereby fully incorporated by reference.

The polysulfones constitute yet another class of thermoplastic polymer components which can be utilized in the present invention. Polysulfones are generally classified as high molecular weight polymers containing sulfone groups and aromatic nuclei in the main polymer chain. The term "polysulfone" also denotes a class of polymers prepared by radical-induced copolymerization of olefins and sulfur dioxide. Polysulfones are generally clear, rigid, tough thermoplastics with generally high glass transition temperatures, i.e., 180° C. to about 250° C., with a chain rigidity generally being derived from the relatively inflexible and immobile phenyl and SO₂ groups. Examples of various polysulfones include bisphenol A polysulfone, polyarylethersulfone, polyethersulfone, polyphenylsulfone, and the like. These and other examples of polysulfones which can be utilized in the present invention are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 13, John Wiley & Sons, Inc., New York, N.Y., 1988, pages 196-211, which is hereby fully incorporated by reference.

The various polybutylene polymers can also be utilized in the present invention and are derived essentially from high molecular weight, predominantly isotactic poly(1-butene) homopolymers or copolymers. These as well as other examples of various polybutylene polymers which can be utilized in the present invention are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 2, John Wiley & Sons, Inc., New York, N.Y., 1985, pages 590-605, which is hereby fully incorporated by reference.

Polyethylene, and the various forms thereof, constitutes another class of thermoplastic copolymers which can be utilized with another thermoplastic copolymer which is immiscible therewith and, at a specific processing temperature, has a different viscosity therefrom. Examples of various types of polyethylene include linear polyethylene such as ultra low density polyethylene, linear low density polyethylene, high density polyethylene, high molecular weight high density polyethylene, ultra high molecular weight polyethylene, and the various types of branched polyethylenes such as low density polyethylene, and the like. These and examples of other polyethylene polymers which can be utilized are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 6, John Wiley & Sons, Inc., New York, N.Y., 1986, pages 383-522, which is hereby fully incorporated by reference.

Still another type or class of thermoplastic polymer component which can be utilized in the present invention is the various polypropylene polymers, such as isotactic polypropylene and the like. It is to be understood that within the classification of polypropylene polymers and polyethylene polymers are the various copolymers of ethylene and propylene. A description of various polypropylene polymers can be found in the Encyclopedia of Polymer Science and Engineering, Vol. 13, John Wiley & Sons, Inc., New York, N.Y., 1988, pages 464-531, which is hereby fully incorporated by reference.

Another thermoplastic polymer component suitable for use in the present invention is polystyrene, including crystal polystyrene, impact polystyrene, and the like. Such polymers are known to the art, and examples thereof suitable for use in the present invention are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 16, John Wiley & Sons, Inc., New York, N.Y., 1989, pages 1-246, which is hereby fully incorporated by reference.

In another aspect of the invention, it has been discovered that surprising improved results are obtained when a modified PET is used, particularly in combination with thermoplastic elastomers. The modified polyethylene terephthalate (M-PET) is a random mixed linear thermoplastic copolyester formed by the reaction of ethylene glycol, terephthalic acid and at least one other glycol and/or dicarboxylic acid. The M-PET has an intrinsic viscosity of from about 0.4 to about 1.2 and a melting point lower than unmodified PET (which is about 265° C.). Desirably the melting point of the M-PET is from about 200° C. to about 255° C., preferably from about 225° C. to about 250° C., and most desirably from about 235° C. to about 248° C.

One or more glycols, in addition to ethylene glycol, may be used alone or in combination with one or more dicarboxylic acids, in addition to terephthalic acid.

Suitable glycols and dicarboxylic acids are any glycol or diacid which is reactive to form a copolyester with PET and interrupts the crystallinity of PET sufficient to lower its melting point. Suitable glycols include aliphatic, cycloaliphatic and aromatic glycols. Aliphatic glycols include straight or branched chain alkane and alkene diols, including 1,3-propanediol; 1,4-butanediol; 1,5-pentanediol; 1,6-hexanediol; 3-methyl-1,5-pentanediol; 2,2-dimethyl-1,3-propanediol; 2-methyl-1,3-propanediol; 3-octyl-1,6-hexanediol; and cyclohexane dimethanol. Aromatics include benzene glycol and ethoxylated bis-phenol A. Polyether glycols such as diethylene glycol may also be used. Although less desirable, triols may be used. The preferred glycols are 1,5-pentanediol and 1,6-hexanediol.

Suitable dicarboxylic acids include aliphatic, straight and branched chain diacids, and aromatics. Exemplary aliphatic diacids include C₄ -C₁₂ diacids, which carbons include the carboxyl groups, such as adipic acid, glutaric acid, sebacic acid, azelaic acid, succinic acid, and 1,12-dodecanedioic acid. The preferred diacids are glutaric or azaleic acid.

Typically, the aromatic dicarboxylic acids have a molecular weight less than about 500 and are aromatic dicarboxylic acids including isophthalic acid (m-phthalic acid), phthalic acid (o-phthalic acid), t-butyl isophthalic acid, 4,4'-dibenzoic acid, 4,4'-substituted dicarboxy compounds with two benzene nuclei such as bis(p-carboxyphenyl)methane, p-oxy(p-carboxyphenyl)benzoic acid, ethylene-bis(p-oxybenzoic acid), 1,5-naphthalene dicarboxylic acid, 2,6-naphthalene dicarboxylic acid, 4,4'-sulfonyl dibenzoic acid, and symmetrically substituted derivatives thereof, with substituents such as C₁ -C₄ alkyl, halo and alkoxy groups. The preferred aromatic dicarboxylic acid is isophthalic acid.

Dicarboxylic acids may also be used which have at least one side chain extending from them. The side chains can be aliphatic or cycloaliphatic and can contain one or more oxygen atoms as an additional element but at least two (2) carbon atoms must be present between oxygens. The side chains may also contain one or more double bonds and can be straight or branched chain. Any common aliphatic, cycloaliphatic or aromatic dicarboxylic acid may be utilized when substituted with the above-described side chains. The molecular weight of the dicarboxylic acid should not be above about 500 excluding the contribution of the side chain.

Specific examples of suitable long chain acids include substituted succinic acids having alkyl or alkenyl radicals of 8-22 carbon atoms in the o-position, 2-(1-dodecyloxy) terephthalic acid, 2-decyl-3-tridecyl succinic acid, 3-decyl-phthalic acid and 1-dodecyl-1,2-cyclohexane dicarboxylic acid.

The term "dicarboxylic acids" as used herein, includes equivalents of dicarboxylic acids having two functional carboxyl groups which perform substantially like dicarboxylic acids in reaction with glycols in forming copolyester polymers. These equivalents include esters and ester-forming derivatives, such as acid halides and anhydrides. While the molecular weight of the diacids suitable for use herein typically have a molecular weight of less than 500, the equivalent ester and ester-forming derivatives may have molecular weight above 500.

Copolyesters of the invention can be prepared by conventional ester interchange and condensation reactions, as set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 12, John Wiley & Sons, Inc., NY, N.Y., 1990 and in U.S. Pat. No. 4,223,126 and U.S. Pat. No. 3,890,279, all of which are incorporated herein by reference.

The amount of glycol, other than ethylene glycol, and/or dicarboxylic acid, other than terephthalic acid, incorporated into the copolyester is an amount sufficient to lower the melting point of an unmodified polyethylene terephthalate, and may vary depending upon the glycol and/or dicarboxylic acid. Generally, however, an amount of glycol and/or dicarboxylic acid from about 1 to about 20 percent by weight of the total copolyester is suitable. Preferably, from about 1 to about 10 percent and most desirably from about 2 to about 6 percent of glycol and/or dicarboxylic acid is present.

In a preferred embodiment, the dicarboxylic acid, other than terephthalic acid, is present in an amount of from about 1% to about 10%, most preferably from about 2% to about 5%, based upon the total weight of acid present in the copolyester and the glycol, other than ethylene glycol, is present in an amount of from about 1% to about 8%, most preferably from about 1% to about 4%, based upon the total glycol in the copolyester.

A preferred copolyester is one comprised of terephthalic acid, ethylene glycol and about 2-5% isophthalic acid, based upon the total weight of acid present. Diethylene glycol may additionally be present, in an amount of from about 1-4% of the total weight of glycol in the copolyester. Such a preferred copolyester will have an intrinsic viscosity of about 0.62 and is commercially available as TRAYTUF® PET resins from The Goodyear Tire and Rubber Company, Akron, Ohio, U.S.A. Particularly suitable is TRAYTUF® 6254C PET resin.

In addition to the polymers described hereinabove, particularly polyurethanes and polyester-ether polymers, other thermoplastic elastomers suitable for combination with the M-PET are block styrenic copolymers, polyether block amides (PEBA) and ethylene propylene diene (EPDM) terpolymers.

Suitable block styrenic copolymers are of the linear or A-B-A type. Basically, these are triblock polymers consisting of a soft rubber or elastomer midblock and hard thermoplastic polystyrene blocks attached to each end. These polymers fall into three basic categories and differ primarily in the type of rubber used in the midblock: styrene-butadiene-styrene (S-B-S); styrene-isoprene-styrene (S-I-S); and styrene-ethylene/butylene-styrene (S-EB-S). Such triblock styrenic copolymers are commercially available from Shell Chemical Company (Texas, U.S.A.) as Kraton® thermoplastic rubber D series (S-B-S and S-I-S) and G series (S-EB-S). These examples of styrenic block copolymers are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 5, John Wiley & Sons, Inc., NY, N.Y., 1990, pages 416-430, which is hereby fully incorporated by reference.

The polyether block amides (PEBA), generally, have a structure consisting of regular and linear chains of rigid polyamide (nylon) block and flexible polyether blocks with the generalized formula ##STR5## wherein PA represents the polyamide block, the PE represents the polyether block, and "n" represents an integer such that the molecular weight of the polymer is between about 20,000 and 50,000. Such polyether block amide copolymers are commercially available, such as Pebax® polyether block amide, manufactured by Atochem Inc. (New Jersey, U.S.A.).

To make the ethylene propylene diene (EPDM) terpolymers, most commonly the dienes 5-ethylidene-2-norbornene (ENB); 1,4-hexadiene (HD); and dicyclopentadiene (DCPD) are used. Although the ratios for the monomers widely varies, most polymers contain 40-90 mol % ethylene and 0-4 mol % diene. Such EPDM terpolymers are commercially available such as Nordel® thermoplastic rubber from DuPont and Vistalon® by Exxon. These and other examples of EPDM polymers are set forth in the Encyclopedia of Polymer Science and Engineering, Vol. 6, John Wiley & Sons, Inc., NY, N.Y., 1990, pages 522-563, which is hereby fully incorporated by reference.

In accordance with the present invention, desirably two, or more, of the above-noted types of thermoplastic polymer components are selected, which, as noted previously, are generally immiscible with respect to one another, have relatively different viscosities at a specific processing temperature, and generally do not degrade at the processing temperature, are blended under high shear to yield a two-phase or multiple-phase composition having fibers incorporated therein and wherein the two, or more, different thermoplastic polymers have good mechanical compatibility to every component, that is, mutually good adhesive properties with respect to each component. Unexpectedly, an extremely smooth surface layer is produced which is substantially and typically free of fibers. Although a large number of combinations of various specific thermoplastic polymers exist, desirable combinations according to the above guidelines can be readily determined by one skilled in the art. Thus, fiber reinforced blends of polyvinyl chloride (including chlorinated polyvinyl chloride) and polycarbonate can be utilized, fiber reinforced blends of polyvinyl chloride (including chlorinated polyvinyl chloride) and ABS type copolymers can be utilized, as well as fiber reinforced blends, as noted above, wherein one component is polyurethane, and the second component is PET, PETG, polycarbonate, polyacetal, or an ABS copolymer. One skilled in the art will appreciate that it is advantageous to combine the M-PET with polymers having a lower melting point than PET. In other words, it is advantageous to use M-PET, instead of PET, in systems where the processing temperature is actually above the degradation temperature of the higher viscosity polymer if PET was used. The lower melting M-PET enables the injection molder to operate within a wider processing window when combining a higher viscosity thermoplastic polymer which has a lower melting point than PET, with the M-PET. Thus, enhanced physical properties of the thermoplastic physical properties of the thermoplastic polymer due to less degradation of the polymer at lower processing temperatures results also. Such suitable combinations of polymers include M-PET combined with a block styrenic copolymer, a polyether block amide, an ethylene propylene diene (EPDM) terpolymer, and a thermoplastic polyurethane.

Even though two component systems are generally preferred, the present invention also encompasses multicomponent compositions having three or more of the above-noted thermoplastic polymer components which are blended under high shear in the presence of fibers. The amount of any thermoplastic polymer component with respect to an immiscible thermoplastic polymer component in a two-component thermoplastic blend according to the preferred embodiment of the present invention is from about 15 percent to about 85 percent by weight, desirably from about 25 to about 75 percent by weight, and preferably from about 40 percent to about 60 percent by weight with the remaining component constituting the difference. For systems using M-PET (thermoplastic copolyester), the amount of M-PET component with respect to the immiscible thermoplastic polymer component is from about 10 percent to about 90 percent by weight, desirably from about 20 percent to about 80 percent, and preferably from about 30 percent to about 70 percent by weight with the remaining component constituting the difference.

When more than two thermoplastic polymer components are utilized, the amount of one of the thermoplastic polymer components is within the above ranges with the remaining two or more thermoplastic components constituting the difference, i.e. the total of all components add up to 100 percent by weight. Desirably, the remaining two or more components each exist in amounts of at least 15 percent, and desirably at least 20 percent or 25 percent by weight.

In accordance with the present invention, short fibers are added to the thermoplastic immiscible polymer components to provide a fiber-reinforced molding composition. The types of organic fibers which can be utilized are limited to those which generally do not melt during blending of the thermoplastic polymer components of the present invention. Examples of such organic fibers include aramid, that is aromatic polyamide fibers, and various aramid hybrides such as aramid/carbon, aramid/carbon/glass, and aramid/glass composites. Generally, any type of inorganic fiber can be utilized including those known to the art and to the literature such as glass fibers. Glass fibers, either unsized or, preferably, sized, and particularly chopped, i.e., short, glass fibers in lengths of about one-eighth inch to two inches, are preferred where an average length of one-eighth to one-half inch fiber is most preferred. Due to the shear mixing with the matrix polymers, especially the viscous immiscible polymer, a majority of the short fibers are broken or sheared into shorter fibers whereby said sheared fibers are typically reduced in size to about 0.2 to about 3 millimeters in length. A common glass fiber which can be utilized is "E" type glass fiber which is substantially free of alkali metal salts and has a tensile strength of about 500,000 psi, a modulus of elasticity of around 10.5 million psi, and a fiber diameter between about 0.0001 and 0.001 inch. Continuous glass roving can also be utilized and subsequently chopped to a desired length. Smaller glass fibers, known as "S" milled fibers, are also commercially available, although the size range is smaller and more narrow, typically between 1/32 and 1/8 inch in length. Other suitable inorganic fibers include carbon fibers, carbon/glass hybrid fibers, boron fibers, graphite fibers, and the like. Various ceramic fibers can also be utilized such as alumina-silica fibers, alumina fibers, silicon carbide fibers, and the like, as well as various metallic fibers such as aluminum fibers, nickel fibers, steel, e.g. stainless steel fibers, and the like. The length of the non-glass fibers is generally the same as the glass fibers and hence initially can be from about 1-8 inch to about 2 inches in length and more desirably have an average length of from about 1/8 to about 1/2 inch before shear blending with the various thermoplastic polymer components. The fibers are combined with the two, or more, thermoplastic polymer components on a weight basis of from about 5 percent to about 60 percent, desirably from about 15 percent to about 50 percent, and preferably from about 25 percent to about 45 percent by weight based upon the total weight of the immiscible thermoplastic polymer components and the fibers. For systems using M-PET, the fibers are combined with the two, or more, thermoplastic polymer components on a weight basis of from about 5 percent to about 60 percent, desirably from about 10 percent to about 50 percent, and preferably from about 20 percent to about 40 percent by weight based upon the total weight of the immiscible thermoplastic polymer components and the fibers.

The fiber-reinforced thermoplastic molding composition blend, etc., is made by initially compounding the various ingredients and making them into a suitable form or shape for storage and subsequent use, and then processing the same at a suitable temperature to form a molded article or end product. The compounding step generally entails adding the two, or more, immiscible thermoplastic components which are utilized as well as the fibers to a mixing or blending apparatus having at least moderate shear, such as a Banbury, a twin-screw extruder, a Buss Kneader, or the like, and mixing the same until generally a two-phase, or a multiple phase, blend having fibers incorporated therein is obtained. The mixing temperature is approximately the same as the processing temperature of the molding operation, although it can be higher or lower, e g., by 10° F. or even 20° F. In order to prevent the various fibers from undue breakage, which reduces the physical properties of the molded end product, or composition, the fibers are generally added after a melt is developed in the blending apparatus, as toward the end of the compounding process Shear mixing is continued until the various components are generally dispersed, and overmixing is avoided because it tends to reduce the fibers to an undesirable short length. The resulting mixture or blend of thermoplastic polymer components and fibers is generally cooled to produce a solid mass and then pelletized or otherwise divided into suitable size particles for use in a molding apparatus used to form the final product or composition, i.e. article.

On an optional basis, minor amounts of other molding additives can be intermixed with the immiscible thermoplastic compounded polymers. For instance, mold release agents can be added to obtain a clean release from the mold platen. Opacifying pigments such as titanium dioxide, or filler pigments such as calcium carbonate, talcs, carbon blacks, silicas, clays, and the like, can be added. Colorants such as tinting pigments or organic dyes can be added to provide color to the molded article Ordinarily such additives, if utilized, comprise less than about 25 percent, desirably less than 15 percent, and preferably less than 10 or 5 percent by weight, of the molding composition based on the weight of matrix polymers plus reinforcing fibers. Other additives, such as up to about 15 percent by weight of Teflon powder, or up to about 2 percent by weight of silicone oil, can be used for compositions for bearings, or up to about 12 percent by weight of stainless steel fibers can be used for conductivity purposes or for shielding against EMR waves.

The compounded immiscible thermoplastic molding compositions containing fibers incorporated therein, as well as the various optional molding additives, as noted above, are generally molded under high shear conditions. That is, the compounding molding step utilizes a moderate to high shear range as from about at least 10, desirably at least 100, desirably at least 500, etc., reciprocal seconds, whereas the actual end product or article formation step such as injection molding generally requires high shear such as a shear rate of at least 100 or 200, desirably at least 500, more desirably at least 800, etc., reciprocal seconds. High shear conditions, that is, shear rates of at least 100 reciprocal seconds, are generally required as a practical matter to obtain the unexpectant smooth surface characteristics of the present invention. Any conventional processing device which typically generates the required high shear processing rates can be utilized Examples include various injection molding machines including those utilizing a plunger or more preferably a reciprocating screw. As long as suitable high shear conditions are generated to produce smooth surface articles or products of the present invention, various injection blow molding machines, and to a lesser extent various compression molding machines, can also be utilized.

The processing temperature will naturally vary depending upon the type of specific different thermoplastic components which are utilized and usually is from about 200° C. to about 300° C. although higher or lower temperatures can be utilized. For example, when a thermoplastic polyurethane is blended with a polycarbonate in the presence of glass fibers, the processing temperature can generally range from about 240° C. to about 260° C. Blending of PVC with polycarbonate and glass fibers can be molded at temperatures at from about 225° C. to about 240° C. Yet another example is a blend of a thermoplastic polyurethane, polyacetal, and glass fibers which typically can be blended at temperatures of from about 240° C. to about 255° C. A blend of a thermoplastic urethane, PET, and glass fibers can be blended at temperatures of from about 245° C. to about 265° C.

For a blend using PET, the injection molding processing window can be widened by using modified PET instead of unmodified PET. The amount by which the processing window is widened will vary depending upon the thermoplastic polymer being used with the M-PET. However, generally the window is widened by 20°-40° F. For example when blending with PET, the window is widened from a range of 490° F. to 505° F. using unmodified PET to 465° F. to 505° F. with M-PET. Thus, M-PET allows a lowered processing temperature by about 15 to about 20 or 25 degrees.

Once the thermoplastic compositions have been molded in accordance with the various aspects of the present invention, e.g. the high shear blending of immiscible thermoplastic components generally having relative different viscosities at a processing temperature which is below the degradation temperature of the thermoplastic components with fibers, yields a mechanically compatible end product unexpectedly having a smooth surface layer containing essentially one thermoplastic component with an interior portion having two phases and containing the fibers therein, have very high physical properties such as impact resistance, high heat distortion temperatures, high tensile modulus, high flexural modulus, and the like. For example, when a thermoplastic polyurethane is compounded with PET on approximately a 50/50 percent weight basis and the two components contain approximately 25 percent by weight of fiber glass therein, the following physical properties are typical: notched Izod impact resistance of 1.0 ft lbs./inch or greater, and generally at least 2.0 ft. lbs./inch at room temperature; heat distortion temperatures of at least 200° F. and generally at least 250° F. at 264 psi; a tensile modulus of at least 700,000 psi, generally at least 1,000,000 psi and even at least 1,500,000 psi; and a flexural modulus of at least 700,000 psi, and generally at least 1,000,000 psi, and even at least 1,200,000 psi. Unexpectedly, by using M-PET with the polyurethane, superior improvement in the impact strength of such compositions is obtained such that the notched and unnotched Izod impact values are two times or greater than formulations with unmodified PET. (See Example 9, Table VI below).

In view of the exceptionally good physical properties such as high stiffness (for example, high tensile modulus and high flexural modulus), high heat distortion temperatures, and excellent melt flow, numerous end uses exist. Moreover, with regard to the exceptionally smooth surface achieved, the same can be maintained, or dulled to provide a low sheen, or altered by texturing the mold surface to provide a pebbled grain or other decorative surface. A particularly desirable end use of the molded compositions of the present invention is for housings, fenders, etc., as well as for horizontal surfaces in a vehicle. Thus, the molded article can be an automotive hood, fender, truck, roof, and the like. The molded compositions of the present invention, inasmuch as they can contain surfaces rich in polyurethane, provide excellent paint adhesion with respect to various industrial paint coatings such as polyurethane-based paints, without the need of a primer.

The invention will be better understood by referring to the following illustrative examples.

EXAMPLE 1 Thermoplastic Urethane/Polycarbonate/Glass Fibers

A composite of 35 percent thermoplastic urethane (TPU), i.e., Estane 58137, manufactured by The B. F. Goodrich Company, which is made from a polyester intermediate utilizing MDI and 1,4-butane diol; 35 percent polycarbonate, i.e., Dow Calibre 300-22; and 30 percent glass fiber was made on a Werner-Pfleiderer compounding twin-screw extruder. The TPU was characterized by its low viscosity of 7-8×10² poise, on a 20/1, L/D, capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The polycarbonate was characterized by its high viscosity of 7-9×10³ poise at 260° C. The glass was 1/4-inch "E" glass.

The TPU and polycarbonate were dried for 2 hours at 100° C. Then the TPU and polycarbonate were mixed on the Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear port of the extruder. Downstream, after these materials were mixed and heated to about 240° C., glass was added. Work and mixing continued on the compounding extruder. This composite blend at 260° C. was extruded through a spaghetti die, cooled in air, and chopped into pellets.

The pellets were dried 2 hours at 105° C. The injection molding was carried out in a physical property mold. The mold temperature was set at 50° C. The melt temperature achieved was 252° C. The glass-filled TPU and glass-filled polycarbonate were made under the same conditions.

Physical data are set forth in Table I.

                  TABLE I                                                          ______________________________________                                         PROPERTIES OF TPU/POLYCARBONATE/GLASS FIBER                                                      35% TPU                                                                        35% Polycar-                                                                              70% Polycar-                                                70% TPU    bonate     bonate                                                   30% Glass                                                                              30% Glass  30% Glass                                         ______________________________________                                                                          Would not                                                                      mold at 252° C.                        Surface Smoothness,                                                                        0.3 microns                                                                              0.4 microns                                                                               4.5 microns*                                  Taylor-Hobson                                                                  Surtronic 10 Gauge                                                             Tensile Strength,                                                                          11,700 psi                                                                               15,000 psi 14,600 psi                                    ASTM D638                                                                      Elongation  12.6%     4.3%       2.3%                                          Tensile Modulus                                                                            520,000 psi                                                                              970,000 psi                                                                               1,080,000 psi                                 Heat Deflection                                                                            116° C.                                                                           141° C.                                                                            145° C.                                Temperature at 264                                                             psi ASTM D698                                                                  annealed at 120° C.                                                     ______________________________________                                          *The polycarbonate would not mold at 252° C., but plugged the           injection sprue. These data are for polycarbonate molded at 271° C      This example shows the excellent smoothness of the TPU/polycarbonate/glas      blend at conditions where the polycarbonate/glass cannot be molded. The        blend has a far superior smooth surface finish to the polycarbonate/glass      molded at a higher temperature. The physical properties of the 35% TPU/35      PC/30% glass blend are also similar to the 70% PC/30% glass blend. Tensil      strength is superior, and the tensile modulus and heat deflection              temperature approach the properties of the PC/glass blend.                     The combination of properties is unique and unexpected with surface and        melt flow similar to the lower viscosity TPU/glass composite and the           physical properties closer to the higher viscosity PC/glass composite.   

EXAMPLE 2 Vinyl/Polycarbonate/Glass Fiber

A composite of 35 percent vinyl compound, i.e., Geon 87241, a polyvinyl chloride compound manufactured by The B. F. Goodrich Company; 35 percent polycarbonate, i.e., Dow Calibre 300-22; and 30 percent glass fiber was made on a Werner-Pfleiderer compounding twin-screw extruder. The vinyl was characterized by its low viscosity of 2-4×10³ poise, on a 20/1, L/D, capillary rheometer at 100 sec⁻¹ shear rate and 230° C. The polycarbonate is characterized by its high viscosity of 3-5×10⁴ poise at 230° C. The glass fibers were 1/4-inch "E" glass.

The polycarbonate was dried for 2 hours at 100° C.; the vinyl was not dried further. The vinyl and polycarbonate were then mixed on the Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear port of the extruder. Downstream, glass fibers were added. Working and mixing continued on the compounding extruder. At 237° C., this composite blend was extruded through a spaghetti die, cooled in air, and chopped into pellets.

A vinyl/glass fiber, at a 70:30 weight ratio, was produced under similar conditions. A polycarbonate/glass fiber control, 70:30 weight ratio, was produced under similar conditions except the melt temperature at the die was 277° C.

The pellets were dried 2 hours at 105° C. The injection molding was carried out in a physical property mold at a temperature of 50° C. The melt temperature was 229° C.

A control compound of vinyl/glass, 70:30 weight ratio, was made under the same conditions. A control compound of polycarbonate/glass, 70:30 weight ratio, was made at 271° C. in a compounding extruder.

Physical data are set forth in Table II.

                  TABLE II                                                         ______________________________________                                         PROPERTIES OF VINYL/POLYCARBONATE/                                             GLASS FIBERS                                                                                      35% Vinyl                                                                      30% Glass  70% Polycar-                                               70% Vinyl                                                                               35% Polycar-                                                                                 bonate                                                  30% Glass                                                                                  bonate  30% Glass                                        ______________________________________                                                                           Would not                                                                      mold at                                                                        229° C.                               Surface Smoothness,                                                                        0.6 microns                                                                               0.7 microns                                                                               4.5 microns*                                 Taylor-Hobson                                                                  Surtronic 10 Gauge                                                             Tensile Strength,                                                                          12,800 psi 13,300 psi 14,600 psi                                   ASTM D638                                                                      Elongation  1.6%       1.3%       2.6%                                         Tensile Modulus                                                                            1,760,000 psi                                                                             2,000,000 psi                                                                             1,080,000 psi                                Heat Deflection                                                                            82° C.                                                                             117° C.                                                                            145° C.                               Temperature @ 264                                                              psi ASTM D698                                                                  Annealed at 93° C.                                                      ______________________________________                                          *The polycarbonate (PC) would not mold at 229° C., but plugged the      injection sprue. These data are for polycarbonate molded at 271° C      These data show that vinyl/polycarbonate/glass blend gives a good surface      at conditions where the polycarbonate/glass cannot be molded. The blend        has a much superior smooth surface finish to polycarbonate/glass molded a      a higher temperature.                                                          The physical properties of the vinyl/PC/glass blend are unexpectedly           higher in modulus than either the vinyl/glass blend or the PC/glass blend      and the heat deflection temperature is higher than the mean heat               deflection temperature of vinyl/glass and PC/glass.                            The combination of properties is unique with surface and melt flow simila      to the lower viscosity vinyl/glass composite and the physical properties       closer to the PC/glass composite.                                        

EXAMPLE 3 Vinyl/Polycarbonate

A composite of 35 percent vinyl compound, i.e., Geon 87241, a polyvinyl chloride compound manufactured by The B. F. Goodrich Company; 35 percent polycarbonate, i.e., Dow Calibre 300-22; and 30 percent glass was made on a Buss Kneader rotating-reciprocating compounding machine. The vinyl compound was characterized by its low viscosity 0.5-1.5×10⁴ poise, on a 20/1, L/D capillary rheometer at 100 sec shear rate at 210° C. The polycarbonate was characterized by its high viscosity, 0.5-1.5×10⁵ poise, on a 20/1, L/D rheometer at 210° C. The glass was 1/4-inch "E" glass.

The vinyl compound and the polycarbonate were mixed on the Buss Kneader. After melting the blend, glass was added through a port on the Buss Kneader and mixed into the blend achieving a compound temperature of 210° C. This compound was injection molded at 210° C. into a cold mold (50° C.) to form a smooth product. The surface roughness was 0.6 microns as measured on a Taylor-Hobson Surtronic 10 roughness gauge. These data show good surface appearance for vinyl/polycarbonate/glass when compounded on a different type compounding machine.

EXAMPLE 4 Vinyl/ABS/Glass

A composite of 35 percent vinyl compound, that is, Geon 87241, a polyvinyl chloride compound manufactured by The B. F. Goodrich Company; 35 percent ABS, that is, Taitalac 6000, manufactured by Bolcof; and 30 percent glass was made on a Buss Kneader compounding machine. The vinyl is characterized by a melt viscosity of 0.5-1.5×10⁴ poise on a 20/1, L/D capillary rheometer at 210° C. The ABS has only a slightly higher viscosity of 1.8×10⁴ poise. The glass was 1/4-inch "E" glass.

The vinyl compound and ABS were mixed on a Buss Kneader compounding machine. After melting the blend, glass was added through a port on the barrel of the Buss Kneader and mixed to a melt temperature of 207° C.

This compound was injection molded at 210° C. into a cold mold (50° C.) to form a plaque with a surface roughness of 0.7 microns as measured on a Taylor-Hobson Surtronic 10 roughness gauge. These data show good surface smoothness for vinyl/ABS/glass when compounded on a different type compounding machine.

EXAMPLE 5 Thermoplastic Urethane/Polyacetal/Glass

A composite of 53 percent polyurethane (Estane 58137), 17 percent polyacetal (Delrin 900), and 30 percent glass fibers was made on a Werner-Pfleiderer compounding twin-screw extruder. The glass was 1/4-inch chopped "E" glass.

The TPU and polyacetal were dried two hours at 100° C. Then the TPU and polyacetal were mixed on the Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear extruder port. Downstream, after these materials were mixed and heated to about 240° C., glass was added. Work and mixing were continued on the compounding extruder. This composite blend was extruded through a spaghetti die at about 260° C., cooled, and chopped into pellets.

The pellets were dried 4 hours at 105° C. The injection molding was carried out in a physical property mold. The mold temperature was set at 45° C. The melt temperature achieved was 250° C.

Physical data are set forth in Table III.

                  TABLE III                                                        ______________________________________                                         PHYSICAL PROPERTIES OF TPU/POLYACETAL/GLASS                                    ______________________________________                                         Surface Smoothness, Taylor-Hobson                                                                     0.2     microns                                         Surtronic 10 Gauge                                                             Tensile Strength, ASTM D638                                                                           7800    psi                                             Elongation             8.5%                                                    Tensile Modulus        560,000 psi                                             Flexural Strength, ASTM D790                                                                          14,700  psi                                             Flexural Modulus       580,000 psi                                             Vicat softening, ASTM D1525B                                                                          159°                                                                            C.                                              Heat Deflection Temperature                                                                           135°                                                                            C.                                              @ 264 psi, ASTM D698                                                           Annealed at 120° C.                                                     Izod impact, ASTM D638                                                         Unnotched              17.7    ft. lbs/in                                      Notched                2.1     ft. lbs/in                                      ______________________________________                                    

This data shows the ability to have an outstandingly smooth surface with 30 percent glass in this TPU/polyacetal blend and include generally good physical properties.

EXAMPLE 6 Thermoplastic Urethane/Polyethylene Terephthalate/Glass

A composite of 35 percent thermoplastic urethane (Estane 58137), 35 percent polyethylene terephthalate (recycled bottle resin), and 30 percent glass fiber was made on a laboratory-size Werner-Pfleiderer compounding twin-screw extruder. The TPU was characterized by its low viscosity of 7-8×10² poise, measured on a 20/1, L/D capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The PET was characterized by its high viscosity of 6-15×10³ poise, measured on a 20/1, L/D capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The glass was 1/4-inch chopped "E" glass.

The TPU and PET were dried for 2 hours at 100° C. Then the TPU and PET were mixed on a Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear extruder port. Downstream, after these materials were mixed and heated to about 240° C., glass was added. Work and mixing were continued on the compounding extruder. At 260° C., this composite blend was extruded through a spaghetti die, cooled in air, and chopped into pellets.

The pellets were dried 2 hours at 105° C. The injection molding was carried out in a physical property mold. The mold temperature was set at 45° C. The melt temperature achieved was 250° C. The glass-filled thermoplastic urethane and glass-filled PET were made under these same conditions.

Physical data are set forth in Table IV.

                  TABLE IV                                                         ______________________________________                                         PROPERTIES OF THERMOPLASTIC URETHANE/                                          POLYETHYLENE TEREPHTHALATE/GLASS                                                                 35% TPU                                                                70% TPU 35% PET   70% PET                                                      30% Glass                                                                              30% Glass 30% Glass                                          ______________________________________                                         Surface Smoothness,                                                                        0.3 microns                                                                              0.3 microns                                                                              *Could not be                                  Taylor-Hobson                   molded at 250° C.                       Surtronic 10 Gauge                                                             Tensile Strength,                                                                          11,700 psi                                                                               9,400 psi 14,700 psi                                     ASTM D638                                                                      Elongation  12.6%     5.8%      4.0%                                           Tensile Modulus                                                                            520,000 psi                                                                              815,000 psi                                                                              1,160,000 psi                                  Heat Deflection                                                                            116° C.                                                                           136° C.                                                                           150+° C.                                Temperature @ 264                                                              psi ASTM D698                                                                  Annealed at 120° C.                                                     ______________________________________                                          *The PET would not mold at 260° C., but plugged the injection           sprue. These data are for PET molded at 274° C.                         This example shows the excellent surface smoothness of the TPU/PET/glass       blend at conditions where the PET cannot even be molded. TPU/PET/glass         blend has much better melt flow than PET/glass and has significantly           better modulus and heat deflection temperature than TPU/glass. This is a       unique and useful combination and is achieved using a mold temperature of      45° C., at a temperature which is far below 110° C. which i      conventional to the art.                                                 

EXAMPLES 8 and 9 Thermoplastic Urethane/Polyethylene Terephthalate/Glass

A composite of 35 percent thermoplastic urethane (Estane 58137), 35 percent polyethylene terephthalate (recycled bottle resin), and 30 percent glass was made on a Werner-Pfleiderer compounding twin-screw extruder. The TPU was characterized by its low viscosity of 7-8×10² poise, measured on a 20/1, L/D capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The PET was characterized by its high viscosity of 6-15×10³ poise, measured on a 20/1, L/D capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The glass was 1/4 inch chopped "E" glass.

The TPU and PET were dried for two hours at 100° C. Then the TPU and PET were mixed on the Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear extruder port. Down stream, after these materials were mixed and heated to about 240° C., glass was added. Work and mixing were continued on the compounding extruder. This composite blend was extruded through an underwater pelletizing die at the end of the extruder, set at about 260° C. The knife chopped the strands into pellets at the die face.

The pellets were dried 4 hours at 105° C. The injection molding was carried out in a physical property mold. The mold temperature was set at 45° C. The melt temperature achieved was 250° C. A second similar example was made wherein the TPU was 30 percent weight, the PET was 30 percent weight, and the glass was 40 percent weight. The molded properties are set forth below:

Physical data are set forth in Table V.

                  TABLE V                                                          ______________________________________                                                         Example 7 Example 8                                                            30% Glass 40% Glass                                            ______________________________________                                         Surface smoothness, Taylor-                                                                      0.2 microns 0.2 microns                                      Hobson Surtronic 10 Gauge                                                      Tensile strength, ATSM D 638                                                                     13,000 psi  17,000 psi                                       Elongation        5.8%        2.6%                                             Tensile modulus   1,000,000 psi                                                                              1,700,000 psi                                    Flexural strength, ASTM D790                                                                     22,000 psi  32,000 psi                                       Flexural modulus  850,000 psi 1,500,000 psi                                    Vicat softening, ASTM D 1525 B                                                                   173° C.                                                                             196° C.                                   Heat Deflection Temperature                                                                      135° C.                                                                             --                                               @ 264 psi, ASTM D 698                                                          annealed at 120° C.                                                     Izod impact, ASTM D 638                                                        unnotched         20 ft. lbs./in.                                                                            15 ft. lbs./in.                                  notched           3 ft. lbs./in.                                                                             3.7 ft. lbs./in.                                 Coefficient of linear thermal                                                                    1.7 × 10.sup.-5 in/                                    expansion -30 to +30° C.,                                                                 in °C.                                                                              --                                               ASTM D 696                                                                     ______________________________________                                    

As apparent from Table V, fiber-reinforced thermoplastic molding compositions were obtained having extremely high tensile modulus, flexural modulus, heat deflection temperatures, impact resistance, and the like, and yet, the surface was extremely smooth. Inasmuch as the surface is essentially urethane-rich, it is readily paintable without being primed.

EXAMPLES 9, 10, 11 and 12 TPU/unmodified PET/glass vs. TPU/modified PET/glass

A composite of thermoplastic polyurethane, polyethylene terephthalate, and glass fiber, in the percentages indicated in Table VI, was made on a pilot scale Werner-Pfleiderer compounding twin-screw extruder. The polyurethane was made from a polyester intermediate utilizing MDI and 1,4-butane diol and sold by The B. F. Goodrich Company as Estane® 58142 polyurethane. The TPU was characterized by its low viscosity of 38 poise, measured on a 20/1, L/D capillary rheometer at 400-500 sec⁻¹ shear rate and 250° C. The polyethylene terephthalate in Examples 9 and 11 was unmodified PET sold by The Goodyear Tire and Rubber Company as TRAYTUF® 5900C resin. The unmodified PET was characterized by its high viscosity of 2000 poise, measured on a 20/1, L/D capillary rheometer at 100 sec⁻¹ shear rate and 260° C. The PET in Examples 10 and 12 was modified PET, that is, a random mixed linear copolyester formed by the reaction of ethylene glycol, terephthalic acid, 205% (based on total acid) isophthalic acid and 1-4% (based upon total glycol) diethylene glycol, sold as TRAYTUF® 6254C resin by The Goodyear Tire and Rubber Company. The modified PET was characterized by its high viscosity of 2,200 poise, measured on a 20/1, L/D capillary rheometer at 400-500 sec⁻¹ shear rate and 270° C. The glass was 1/8-inch chopped "E" glass. 0.1-0.3% of carbon black as colorant.

Prior to compounding the TPU and PET were dried for 6 hours at 100° C. Then the TPU and PET were mixed on a Werner-Pfleiderer compounding twin-screw extruder, adding granules of these materials at the rear extruder port. Downstream, after these materials were mixed and heated to about 240° C., glass was added. Mixing and compounding was continued in the extruder and at 260° C., this composite blend was extruded through a spaghetti die, cooled in air, and chopped into pellets.

The pellets were dried 6 hours at 105° C. The injection molding was carried out in a physical property mold. The mold temperature was set at 45° C. The melt temperature achieved was 250° C.

Physical data are set forth in Table VI.

                                      TABLE VI                                     __________________________________________________________________________     PROPERTIES OF TPU/PET/GLASS vs. TPU/M-PET/GLASS                                             Ex 9  Ex 10  Ex 11 Ex 12                                                       18% TPU                                                                              18% TPU                                                                               35% TPU                                                                              35% TPU                                                     42% PET                                                                              42% M-PET                                                                             35% PET                                                                              35% M-PET                                                   40% glass                                                                            40% glass                                                                             30% glass                                                                            30% glass                                      __________________________________________________________________________     Flexural Modulus, PSI                                                                       1,649,000                                                                            1,442,000                                                                             849,000                                                                              778,500                                        (ASTM D790)                                                                    Flexural Strength, PSI                                                                        27,600                                                                               28,130                                                                               20,800                                                                               20,820                                        (ASTM D790)                                                                    Izod Impact @ RT                                                               Ft-lb/in.                                                                      Unnotched    7.2   16.2   10.2  26.50                                          Notched      1.9    4.8    2.9   6.24                                          (ASTM D256, Method A)                                                          Heat Distortion                                                                Temperature @ 264 PSI                                                          (ASTM D698 C.°)                                                         Unannealed    50    67     69    72                                            Annealed @   170   162    148   142                                            250° F., 24 hrs.                                                        __________________________________________________________________________

EXAMPLE 13

The ratio of viscosity of M-PET to TPU was determined for shear rates considered standard for high shear compounding and injection molding. The results are summarized below in Table VII.

                  TABLE VII                                                        ______________________________________                                         VISCOSITY VS. SHEAR RATE OF M-PET                                              AND TPU AT 250° C.                                                                 VISCOSITY                                                           (Sec.sup.-1)                                                                              (Pascal-Sec)  VISCOSITY RATIO                                       SHEAR RATE M-PET     TPU     M-PET/TPU                                         ______________________________________                                          200       850       44      19.3                                               500       700       38      18.4                                              1000       380       31      12.3                                              3000       170       26      6.5                                               ______________________________________                                    

Measurements were made using a Monsanto Processibility Tester (MPT) at 250° C. Shear rates ranging from 200 to 500 reciprocal second (sec⁻¹) are generally considered as high shear compounding. For injection molding, the shear rates normally fall into the range of 1000 to 3000 sec⁻¹. The M-PET was Traytuf® 6254C PET resin, a copolyester of terephthalic acid, ethylene glycol and isdphthalic acid. The TPU was a polyester polyurethane commercially available as Estane® 58142 polyurethane resin from the B. F. Goodrich Company, Akron, Ohio, U.S.A.

As can be seen from the results, the viscosity ratios of M-PET to TPU at 250° C. ranged from 6.5 to 19.3, at corresponding shear rates from 3000 sec⁻¹ to 200 sec⁻¹.

As will be appreciated by one skilled in the art, the difference in viscosity between the M-PET and TPU is great enough to achieve a finished product with a TPU surface, but not too great to cause severe separation of the two polymers.

While in accordance with the Patent Statutes, the best mode and preferred embodiment has been set forth, the scope of the invention is not limited thereto, but rather by the scope of the attached claims. 

What is claimed is:
 1. A thermoplastic molding composition, comprising:a fiber-reinforced blend containing a thermoplastic copolyester with at least one immiscible thermoplastic polymer component, said blend containing an effective amount of said fibers to improve physical properties thereof and being prepared in the presence of at least moderate shear, said thermoplastic copolyester formed by the reaction of ethylene glycol, terephthalic acid and at least one other glycol and/or dicarboxylic acid, and said immiscible thermoplastic polymer component being selected from thermoplastic polyurethane, polyester-ether polymers, block styrenic copolymers, polyether block amide, or ethylene propylene diene, said blend having a smooth surface essentially free of fibers when molded at high shear.
 2. A thermoplastic molding composition according to claim 1 wherein the melting point of the copolyester is from about 200° C. to about 255° C.
 3. A thermoplastic molding composition according to claim 2 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester are an alkane diol or a polyether glycol and/or an aromatic dicarboxylic acid.
 4. A thermoplastic molding composition according to claim 2 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester is diethylene glycol and/or isophthalic acid.
 5. A thermoplastic molding composition according to claim 4 wherein the immiscible thermoplastic polymer is polyurethane.
 6. A thermoplastic molding composition according to claim 5 wherein said isophthalic acid is present in an amount of from about 2-5% of the total weight of acid in the copolyester and said diethylene glycol is present in an amount of from about 1-4% of the total weight of glycol in the copolyester.
 7. A thermoplastic molding composition according to claim 1, wherein the amount of said thermoplastic copolyester is from about 10 percent to about 90 percent by weight and wherein the amount of said at least one immiscible thermoplastic polymer component is from about 90 percent to about 10 percent by weight based upon the total weight of said thermoplastic copolyester and said at least one immiscible thermoplastic polymer component, and wherein the amount of said fibers is from about 5 percent to about 60 percent by weight based upon the total weight of said thermoplastic copolyester, said at least one immiscible thermoplastic polymer component and said fibers.
 8. A thermoplastic molding composition according to claim 7, wherein the amount of said thermoplastic copolyester is from about 30 percent to about 70 percent by weight and wherein the amount of said at least one immiscible thermoplastic polymer component is from about 70 percent to about 30 percent by weight based upon the total weight of said thermoplastic copolyester and said at least one immiscible thermoplastic polymer component, and wherein the amount of said fibers is from about 10 percent to about 50 percent by weight based upon the total weight of said thermoplastic copolyester, said at least one immiscible thermoplastic polymer component and said fibers.
 9. A thermoplastic molding composition according to claim 8, wherein said fibers are glass fibers.
 10. A thermoplastic molding composition according to claim 9, wherein said thermoplastic copolyester has a viscosity at said high shear at a processing temperature which is different than said at least one immiscible thermoplastic polymer component and wherein the viscosity ratio of said high viscosity component to said relatively low viscosity component is from about 1.5 to about 200 during molding.
 11. A thermoplastic molding composition according to claim 1, wherein the amount of said thermoplastic copolyester is from about 20 percent to about 80 percent by weight and wherein the amount of said at least an immiscible thermoplastic polymer component is from about 80 percent to about 20 percent by weight based upon the total weight of said thermoplastic copolyester and said at least one immiscible thermoplastic polymer component, and wherein the amount of said fibers is from about 20 percent to about 40 percent by weight based upon the total weight of said thermoplastic copolyester, said at least one immiscible thermoplastic polymer component, and said fibers.
 12. A thermoplastic molded article, comprising:a fiber-reinforced thermoplastic blend in the form of an article having a smooth surface essentially free of said fibers, said thermoplastic blend containing from about 10 to about 90 percent by weight of a thermoplastic copolyester component and from about 90 percent to about 10 percent by weight of an immiscible thermoplastic polymer component based upon the total weight of said thermoplastic copolyester component and said immiscible thermoplastic polymer component, said thermoplastic copolyester formed by the reaction of ethylene glycol, terephthalic acid and at least one other glycol and/or dicarboxylic acid, said immiscible thermoplastic component being polyurethane, block styrenic copolymers, polyether block amide, polyester-ether polymers, or ethylene propylene diene, the amount of said fibers in said blend being from about 5 percent to about 60 percent by weight based upon the total weight of said thermoplastic copolyester component, said immiscible thermoplastic polymer component and said fibers, said blend of said thermoplastic copolyester, said immiscible thermoplastic polymer component, and said fibers being prepared in the presence of high shear.
 13. A thermoplastic molded article according to claim 12, wherein the amount of said thermoplastic copolyester component is from about 30 percent to about 70 percent by weight and wherein the amount of said immiscible thermoplastic polymer component is from about 70 percent to about 30 percent by weight based upon the total amount by weight of said thermoplastic copolyester component and said immiscible thermoplastic polymer component, and wherein the amount of said fibers is from about 15 percent to about 50 percent by weight based upon the total weight of said thermoplastic copolyester component, said immiscible thermoplastic polymer component, and said fibers.
 14. A thermoplastic molded article according to claim 13, wherein said immiscible thermoplastic polymer component is polyurethane, and wherein said fibers are glass fibers.
 15. A thermoplastic molded article according to claim 12, wherein said thermoplastic copolyester component and said immiscible thermoplastic polymer component have a different viscosity in the presence of said high shear at a processing temperature, and wherein the viscosity ratio of said high viscosity component to said low viscosity component is from about 1.5 to about
 200. 16. A thermoplastic molded article according to claim 15, wherein said thermoplastic copolyester component and said immiscible thermoplastic polymer component have a different viscosity in the presence of said high shear at a processing temperature, and wherein the viscosity ratio of said high viscosity component to said low viscosity component is from about 5 to about
 50. 17. A thermoplastic molded article according to claim 12 wherein the melting point of the copolyester is from about 200° C. to about 255° C.
 18. A thermoplastic molded article according to claim 17 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester are an alkane diol or a polyether glycol and/or an aromatic dicarboxylic acid.
 19. A thermoplastic molded article according to claim 18 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester is diethylene glycol and/or isophthalic acid.
 20. A thermoplastic molded article according to claim 19 wherein said isophthalic acid is present in an amount of from about 2-5% of the total weight of acid in the copolyester and said diethylene glycol is present in an amount of from about 1-4% of the total weight of glycol in the copolyester.
 21. A process for molding a thermoplastic molded article, comprising the steps of:a) blending under high shear reinforcing fibers with from about 10 percent to about 90 percent by weight of a thermoplastic copolyester and from about 90 percent to about 10 percent by weight of at least one immiscible thermoplastic polymer component based upon the total weight of said thermoplastic copolyester and said immiscible thermoplastic polymer component, said immiscible thermoplastic polymer component being polyurethane, polyester-ether polymers block styrenic copolymer, polyether block amide or ethylene propylene diene, the amount of said fibers in said blend being from about 5 percent to about 60 percent by weight based upon the total weight of said thermoplastic copolyester, said immiscible thermoplastic polymer component and said fibers, and b) forming an article having a smooth surface layer essentially free of said fibers; wherein said copolyester is formed by the reaction of ethylene glycol, terephthalic acid and at least one other glycol and/or dicarboxylic acid.
 22. The process according to claim 21, wherein said high shear is a shear rate of at least 100 reciprocal seconds.
 23. A process according to claim 22, wherein the amount of said thermoplastic copolyester is from about 30 to about 70 percent by weight and wherein said immiscible thermoplastic polymer component is from about 70 to about 30 percent by weight based upon the total weight of said thermoplastic copolyester and said immiscible thermoplastic polymer component, and wherein the amount of said fibers is from about 15 percent to about 50 percent by weight based upon the total weight of said thermoplastic copolyester, said immiscible thermoplastic polymer component and said fibers.
 24. A process according to claim 23, wherein said immiscible thermoplastic polymer component is polyurethane and wherein said fibers are glass fibers.
 25. A process according to claim 24, wherein said thermoplastic copolyester and said immiscible thermoplastic polymer component have a different viscosity in the presence of said high shear at a processing temperature, and wherein the viscosity ratio of said high viscosity component to said relatively low viscosity component is from about 5 to about
 50. 26. The process according to claim 21 wherein the melting point of said copolyester is from about 200° C. to about 255° C.
 27. The process according to claim 26 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester are an alkane diol or a polyether glycol and/or a aromatic dicarboxylic acid.
 28. The process according to claim 27 wherein said at least one other glycol and/or dicarboxylic acid of said copolyester is diethylene glycol and/or isophthalic acid. 